【作者】：Xinxin He, Pengfei Cheng, Geyu Lu, Fengmin Liu
【题目】：Synthesis of Nest-Like NiO and Its Application on P-Type Dye-Sensitized Solar Cell
【关键词】：Nest-like nickel oxide,dye-sensitized solar cell,nickel oxide film
【版面信息】：Key Engineering Materials 519 (2012) 61-64
摘要:
The nest-like NiO was successfully prepared by calcining the Ni(OH)2precursor synthesized using wet chemical deposition method. A NiO-based p-type dye-sensitized solar cell was fabricated. The photocathode films were coated by doctor-blading NiO paste onto the FTO substrates. The thickness of NiO film was controlled by repeatedly blade coating using one layer of tape. The results manifested that the thickness of the NiO film significantly influenced the photoconversion efficiency. The solar cell based on the NiO film with 13 thickness showed the highest photoconversion efficiency. In addition, the influence of the dye is also investigated. The NiO films were sensitized with C343, N3, and Z907, respectively. The measurement of photocurrent density-voltage characteristics indicated that the highest photoconversion efficiency is about 0.027% using C343 sensitized.